PA0835HD

Date:2015/1/27 18:52:39 Hits:745
Processing Aid Concentrate

Description 

PA0835HD masterbatch is made of HDPE ,fluorin-elastomer and antioxidants, it is a highly effective processing aid for HDPE and MDPE extrusion.

Appearance
Colorless, translucence
Pellets

Applications
Even without increasing the screw speed the output can be increased remarkably. Meanwhile, the pressure build-up in the barrel is reduced. The result is a tremendous increase of the screw lifetime. PH0835HD can effectively prevent the build-up of deposits in the die which are caused by high pigment concentration, flame retardant, blowing agent and other additives.The mixture of different density polyethylene, the suitable dose of PA0835HD will get a remarkably improved processing performance and surface quality.

Addition levels
For uncross-linked polyethylene, 1.0-3.0% PA0835HD has to be dosed.For PEX, the following method are recommended:
A blending of 10% PA0835HD and 90% PE has to be run for 20-30min through the machine at high speed before production.
Starting production 0.5-2.0% PA0835HD has to be dosed. After normal production,the level of dose can be reduced gradually.

Combinations
PA0835HD is compatible with most plastic additives. With H.A.L.S and certain antistatic, the effectiveness of PA0835HD may be reduced.

Packing
PA0835HD is supplied in 25kg PE bags.

Storage
The storage of PA0835HD causes no problem. It is not sensitive to ambient temperature and humidity. At maximum room temperature of 25℃ the storage life is 18 months.

Toxicity/permission
No poison. According to the US-FDA and BgVV, the max dosage level is 10% for food touched application.
??
??
??
Previous:Nothing
Next:Nothing
 
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
The following methods are mainly used for cross-linking Polyethylene
The rules of gel content for different cross-linking techniques
The processes of silane cross-linking polyethylene
Can PEX-material be dried
The influence factors of gel content of silane cross-linking polyethylene
Mixing of grafted material and masterbatches
How to reduce the premature cross-linking of PEX
How to improve the surface quality of the pipes
How to reduce the internal stress of pipes
What about standards of PEX pipe
What kind of joint techniques are available for PEX pipes
PEX pipes are used in the following applications:
The corrosion resistance of PEX
The shrinkage of PEX pipe
Advices on trial of PEX
成人在线偷拍自拍视频 国产自拍视频在线一区 最新2018啪啪自拍视频